Phase formation, crystal structures and magnetic properties of perovskite-type phases in the system La2Co1+z(MgxTi1-x)1-zO6 [Elektronisk resurs]

• Perovskite-type cobaltates in the system La(2)Co(1+z) (Mg(x)Ti(1-x))(1-z)O(6) were studied for z=0 <= x <= 0.6 and 0 <= x <= 0.9, using X-ray and neutron powder diffraction, electron diffraction (ED), magnetic susceptibility measurements and X-ray absorption near-edge structure (XANES) spectroscopy. The samples were synthesised using the citrate route in air at 1350 degrees C. The space group symmetry of the structure changes from P2(1)/n via Pbnm to R (3) over barc with both increasing Mg content and increasing Co content. The La(2)Co(Mg(x)Ti(1-x))O(6) (z=0) compounds show anti-ferromagnetic couplings of the magnetic moments for the Co below 15 K for x=0, 0.1 and 0.2. XANES spectra show for the compositions 0 <= x <= 0.5 a linear decrease in the L(3)/(L(3)+ L(2))Co-L(2.3) edge branching ratio with x, in agreement with a decrease of the average Co ion spin-state, from a high-spin to a lower-spin-state, with decreasing nominal Co(2+) ion content. 

Ämnesord

Natural Sciences  (hsv)

Chemical Sciences  (hsv)

Inorganic Chemistry  (hsv)

Naturvetenskap  (hsv)

Kemi  (hsv)

Oorganisk kemi  (hsv)

Natural Sciences  (hsv)

Chemical Sciences  (hsv)

Physical Chemistry  (hsv)

Naturvetenskap  (hsv)

Kemi  (hsv)

Fysikalisk kemi  (hsv)

Natural Sciences  (hsv)

Chemical Sciences  (hsv)

Materials Chemistry  (hsv)

Naturvetenskap  (hsv)

Kemi  (hsv)

Materialkemi  (hsv)

NATURAL SCIENCES  (svep)

Chemistry  (svep)

Inorganic chemistry  (svep)

Solid state chemistry  (svep)

NATURVETENSKAP  (svep)

Kemi  (svep)

Oorganisk kemi  (svep)

Fasta tillståndets kemi  (svep)

Inorganic Chemistry  (su)

oorganisk kemi  (su)

Materials Chemistry  (su)

materialkemi  (su)

Indexterm och SAB-rubrik

Cobaltates

perovskite

X-ray diffraction

neutron diffraction

magnetic susceptibility

electron diffraction

XANES