KCl-Induced High Temperature Corrosion Behavior of HVAF-Sprayed Ni-Based Coatings in Ambient Air [Elektronisk resurs]

<p>This article is an invited paper selected from presentations at the 2017 International Thermal Spray Conference, held June 7–9, 2017, in Düsseldorf, Germany, that has been expanded from the original presentation.</p>
Published
KK-stiftelsen [SCoPe: Dnr 20160201]
gratis
KCl-induced high temperature corrosion behavior of four HVAF-sprayed Ni-based coatings (Ni21Cr, Ni5Al, Ni21Cr7Al1Y, and Ni21Cr9Mo) under KCl deposit has been investigated in ambient air at 600°C up to 168h. The coatings were deposited onto 16Mo3 steel - a widely used boiler tube material.Uncoated substrate, 304L and Sanicro25 were used as reference materials in the test environment.SEM/EDS and XRD techniques were utilized to characterize the as-sprayed and exposed samples.The results showed that the small addition of KCl significantly accelerated degradation to the coatings. All coatings provided better corrosion resistance compared to the reference materials. The alumina-forming Ni5Al coating under KCl deposit was capable of forming a more protective oxide scale compared to the chromia-forming coatings as penetration of Cl through diffusion paths was hindered. Both active corrosion and chromate formation mechanisms were found to be responsible for Page 1 of 23ASM the corrosion damages. The corrosion resistance of the coatings based on the microstructure analysis and kinetics had the following ranking (from the best to worst): Ni5Al >Ni21Cr> Ni21Cr7Al1Y>Ni21Cr9Mo.

Del av/supplement till:channel record
Ingår i:VärdpublikationJournal of thermal spray technology (Print)27:3, 500-5111059-9630
Ingår i:Värdpublikation

Inställningar Hjälp

Beståndsinformation saknas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.