Bio-coal as an alternative reducing agent in the blast furnace [Elektronisk resurs]

El-Tawil, Asmaa (författare)
Sundqvist Öqvist, Lena (preses)
Björkman, Bo (preses)
Saxen, Henrik (opponent)
Luleå tekniska universitet Institutionen för samhällsbyggnad och naturresurser (utgivare)
ISBN 9789177905707
Publicerad: Luleå : Luleå University of Technology, 2020
Engelska 67
Serie: Licentiate thesis / Luleå University of Technology, 1402-1757 1402-1757
Läs hela texten
Läs hela texten
  • E-bokAvhandling(Lic.-avh. (sammanfattning), 2020)
Sammanfattning Ämnesord
Stäng  
  • The steel industry is aiming to reduce CO 2 emissions by different means; in the short-term, by replacing fossil coal with highly reactive carbonaceous material like bio-coal (pretreated biomass) and, in the longer term, by using hydrogen. The use of bio-coal as part of top charged briquettes also containing iron oxide has the potential to lower the thermal reserve zone temperature of the Blast furnace (BF) and, due to improved gas efficiency, thereby give a high replacement ratio to coke. In order to select a suitable bio-coal to be contained in agglomerates with iron oxide, the current study aims at investigating the devolatilization behavior and related kinetics of different types of bio-coals. In addition, the aim is to investigate the self-reduction behavior of bio-coal-containing iron ore composite under inert condition and simulated blast furnace thermal profile. In the BF the temperature of the top-charged material will increase rather quickly during the descent in the upper part. Ideally, all the carbon and hydrogen contained in the top-charged bio-coal should contribute to the reduction. The devolatilization of bio-coal is thus important to understand and to compare between different types of bio-coal. To explore the devolatilization behavior for different materials, a thermogravimetric analyzer equipped with a quadrupole mass spectrometer was used to monitor the weight loss and off-gases during non-isothermal tests for bio-coals having different contents of volatile matter. The samples were heated in an inert atmosphere up to 1200°C at three different heating rates: 5, 10 and 15°C/min. The thermogravimetric data were evaluated by using the Kissinger–Akahira–Sonuse (KAS) iso-conversational model and the activation energy was determined as a function of the conversion degree. Bio-coals with both low and high content of volatile matter can produce reducing gases that can contribute to the reduction of iron oxide in bio-agglomerates. Bio-coals containing a higher content of catalyzing components such as CaO and K 2 O will enhance the devolatilization and release of volatile matter at a lower temperature.  The self–reduction of composites was investigated by thermogravimetric analyses in argon atmosphere up to 1100°C and evolved gases were monitored by means of quadrupole mass spectroscopy. Composites with and without 10% bio-coal and sufficient coke breeze to keep the C/O molar ratio equal to one were mixed and Portland cement was used as a binder. To explore the effect of added bio-coals, interrupted vertical tube furnace tests were conducted in a nitrogen atmosphere at temperatures selected based on thermogravimetric results, using a similar thermal profile as for the thermogravimetric analyzer. The variation between fixed carbon, volatile matter contents and ash composition for different types of bio-coal influences the reduction of iron oxide. The results showed that the self-reduction proceeds more rapidly in the bio-coal-containing composite and that the volatile matter could have contributed to the reduction. The self-reduction of bio-coal-containing composites started at 500°C, while it started at 740°C with coke as the only carbon source. The hematite was successfully reduced to metallic iron at 850°C with bio-coal present as a reducing agent, but not until 1100°C when using coke. Use of bio-coal with high content of volatile matter but low content of catalyzing elements as potassium, sodium and calcium in bio-agglomerates for the BF can be recommended because it enhances the self-reduction of iron oxide, e.g., wustite was detected by XRD analysis in samples treated up to 680°C. Bio-coal with low content of volatile matter, low alkalis, low phosphorous and high content of fixed carbon will also be suitable to use in the BF.   

Ämnesord

Engineering and Technology  (hsv)
Materials Engineering  (hsv)
Metallurgy and Metallic Materials  (hsv)
Teknik och teknologier  (hsv)
Materialteknik  (hsv)
Metallurgi och metalliska material  (hsv)
Process Metallurgy  (ltu)
Processmetallurgi  (ltu)

Genre

government publication  (marcgt)

Indexterm och SAB-rubrik

Devolatilization
torrefied biomass
bio-coal
volatile matter
reduction
blast furnace
Inställningar Hjälp

Titeln finns på 1 bibliotek. 

Bibliotek i norra Sverige (1)

Ange som favorit
Om LIBRIS
Sekretess
Blogg
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Sondera
Uppsök

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy