Aligned biodegradable cellulose-reinforced nanocomposites with high strength and toughness [Elektronisk resurs]

Geng, Shiyu (författare)
Marcus Wallenberg Prize (MWP) Event 2017 – Young Researchers’ Challenge; October 24–27, 2017, Stockholm, Sweden 
Yao, Kun (författare)
Harila, Maria (författare)
Noël, Maxime (författare)
Zhou, Qi (författare)
Oksman, Kristiina (författare)
Luleå tekniska universitet Institutionen för teknikvetenskap och matematik (utgivare)
Luleå tekniska universitet (utgivare)
Alternativt namn: LTU
Alternativt namn: Engelska Luleå University of Technology
Se även: Högskolan i Luleå (tidigare namn)
2017
Engelska.
Läs hela texten
Läs hela texten
  • E-bok
Sammanfattning Ämnesord
Stäng  
  • Cellulose, as the most abundant component in wood, has attracted a lot of attention for utilizing it in environmentally-friendly applications to replace the fossil-based materials. Nanocellulose materials with high stiffness and strength, large surface area and biodegradability, are promising reinforcement in polymers. However, the energy consumption of nano-scale isolation of cellulose and the dispersion of nanocellulose materials in the polymers are still challenging for obtaining low-cost and ultra-strong nanocomposites. To overcome these, we focus on investigating the aligned nanocomposites reinforced by a very low cellulose nanofibers (CNF) content (0.1 wt%), and grafting polyethylene glycol (PEG) on CNF was performed to improve the dispersion of them. We found that the alignment can improve mechanical properties of the polylactic acid (PLA)/CNF composites dramatically. With a draw ratio of 8, the strength of the aligned composite reached 320 MPa and the toughness was 30 times enhanced compared to the isotropic material. Much better dispersion of the CNF grafted with PEG in PLA matrix was confirmed by scanning electron microscopy (SEM) compared to the ungrafted CNF, and further supported by the mechanical testing results. Furthermore, the aligned nanocomposites exhibited light scattering behavior indicating they have the potential to be used in optical applications. 

Ämnesord

Medical and Health Sciences  (hsv)
Medical Biotechnology  (hsv)
Biomaterials Science  (hsv)
Medicin och hälsovetenskap  (hsv)
Medicinsk bioteknologi  (hsv)
Biomaterialvetenskap  (hsv)
Engineering and Technology  (hsv)
Industrial Biotechnology  (hsv)
Bio Materials  (hsv)
Teknik och teknologier  (hsv)
Industriell bioteknik  (hsv)
Biomaterial  (hsv)
Trä och bionanokompositer  (ltu)
Wood and Bionanocomposites  (ltu)
Inställningar Hjälp

Uppgift om bibliotek saknas i LIBRIS

Kontakta ditt bibliotek, eller sök utanför LIBRIS. Se högermenyn.

Om LIBRIS
Sekretess
Blogg
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Sondera
Uppsök

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy