Chemical composition, crystallinity and thermal degradation of bleached and unbleached kenaf bast (Hibiscus cannabinus) pulp and nanofiber [Elektronisk resurs]

Jonoobi, Mehdi (författare)
Harun, Jalaludin (författare)
Mishra, Manju (författare)
Oksman, Kristiina (författare)
Luleå tekniska universitet Institutionen för teknikvetenskap och matematik (utgivare)
2009
Engelska.
Ingår i: BioResources. - 1930-2126. ; 4:2, 626-639
Läs hela texten
Läs hela texten
Läs hela texten
  • E-artikel/E-kapitel
Sammanfattning Ämnesord
Stäng  
  • Kenaf (Hibiscus cannabinus) nanofibers were isolated from unbleached and bleached pulp by a combination of chemical and mechanical treatments. The chemical methods were based on NaOH-AQ (anthraquinone) and three-stage bleaching (DEpD) processes, whereas the mechanical techniques involved refining, cryo-crushing, and high-pressure homogenization. The size and morphology of the obtained fibers were characterized by environmental scanning electron microscopy (ESEM) and transmission electron microscopy (TEM), and the studies showed that the isolated nanofibers from unbleached and bleached pulp had diameters between 10-90 nm, while their length was in the micrometer range. Fourier transform infrared (FTIR) spectroscopy demonstrated that the content of lignin and hemicellulose decreased in the pulping process and that lignin was almost completely removed during bleaching. Moreover, thermogravimetric analysis (TGA) indicated that both pulp types as well as the nanofibers displayed a superior thermal stability as compared to the raw kenaf. Finally, X-ray analyses showed that the chemo-mechanical treatments altered the crystallinity of the pulp and the nanofibers: the bleached pulp had a higher crystallinity than its unbleached counterpart, and the bleached nanofibers presented the highest crystallinity of all the investigated materials. 

Ämnesord

Engineering and Technology  (hsv)
Industrial Biotechnology  (hsv)
Bio Materials  (hsv)
Teknik och teknologier  (hsv)
Industriell bioteknik  (hsv)
Biomaterial  (hsv)
Trä och bionanokompositer  (ltu)
Wood and Bionanocomposites  (ltu)
Inställningar Hjälp

Beståndsinformation saknas

Om LIBRIS
Sekretess
Blogg
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Sondera
Uppsök

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy