KCl-Induced High Temperature Corrosion Behavior of HVAF-Sprayed Ni-Based Coatings in Ambient Air [Elektronisk resurs]

Jafari, Reza (författare)
International Thermal Spray Conference & Exposition, ITSC 2017, Düsseldorf, Germany, June 7-9, 2017 
Sadeghimeresht, Esmaeil, 1985- (författare)
Shahrabi Farahani, Taghi (författare)
Huhtakangas, Matti (författare)
Markocsan, Nicolaie, 1967- (författare)
Joshi, Shrikant V., 1960- (författare)
PTW (medarbetare)
PTW (medarbetare)
PTW (medarbetare)
Högskolan Väst Institutionen för ingenjörsvetenskap (utgivare)
Publicerad: Springer, 2018
Engelska.
Ingår i: Journal of thermal spray technology (Print). - 1059-9630. ; 27:3, 500-511
Läs hela texten
Läs hela texten
Läs hela texten
  • E-artikel/E-kapitel
Sammanfattning Ämnesord
Stäng  
  • KCl-induced high temperature corrosion behavior of four HVAF-sprayed Ni-based coatings (Ni21Cr, Ni5Al, Ni21Cr7Al1Y, and Ni21Cr9Mo) under KCl deposit has been investigated in ambient air at 600°C up to 168h. The coatings were deposited onto 16Mo3 steel - a widely used boiler tube material.Uncoated substrate, 304L and Sanicro25 were used as reference materials in the test environment.SEM/EDS and XRD techniques were utilized to characterize the as-sprayed and exposed samples.The results showed that the small addition of KCl significantly accelerated degradation to the coatings. All coatings provided better corrosion resistance compared to the reference materials. The alumina-forming Ni5Al coating under KCl deposit was capable of forming a more protective oxide scale compared to the chromia-forming coatings as penetration of Cl through diffusion paths was hindered. Both active corrosion and chromate formation mechanisms were found to be responsible for Page 1 of 23ASM the corrosion damages. The corrosion resistance of the coatings based on the microstructure analysis and kinetics had the following ranking (from the best to worst): Ni5Al >Ni21Cr> Ni21Cr7Al1Y>Ni21Cr9Mo. 

Ämnesord

Engineering and Technology  (hsv)
Materials Engineering  (hsv)
Manufacturing, Surface and Joining Technology  (hsv)
Teknik och teknologier  (hsv)
Materialteknik  (hsv)
Bearbetnings-, yt- och fogningsteknik  (hsv)
Metallurgy and Metallic Materials  (hsv)
Metallurgi och metalliska material  (hsv)
Composite Science and Engineering  (hsv)
Kompositmaterial och -teknik  (hsv)
Manufacturing and materials engineering  (hv)
Produktions- och materialteknik  (hv)
Production Technology  (hv)
Produktionsteknik  (hv)

Genre

government publication  (marcgt)
Inställningar Hjälp

Beståndsinformation saknas

Om LIBRIS
Sekretess
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Uppsök

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy