Ice-Templated Cellulose Nanofiber Filaments as a Reinforcement Material in Epoxy Composites [Elektronisk resurs]

Nissilä, Tuukka (författare)
Wei, Jiayuan (författare)
Geng, Shiyu (författare)
Teleman, Anita (författare)
Oksman, Kristiina, 1959- (författare)
Wood and bionanocomposites (medarbetare)
Wood and bionanocomposites (medarbetare)
Luleå tekniska universitet Institutionen för teknikvetenskap och matematik (utgivare)
Publicerad: MDPI, 2021
Engelska.
Ingår i: Nanomaterials. ; 11:2
Läs hela texten
Läs hela texten
Läs hela texten
  • E-artikel/E-kapitel
Sammanfattning Ämnesord
Stäng  
  •  Finding renewable alternatives to the commonly used reinforcement materials in composites is attracting a significant amount of research interest. Nanocellulose is a promising candidate owing to its wide availability and favorable properties such as high Young’s modulus. This study addressed the major problems inherent to cellulose nanocomposites, namely, controlling the fiber structure and obtaining a sufficient interfacial adhesion between nanocellulose and a non-hydrophilic matrix. Unidirectionally aligned cellulose nanofiber filament mats were obtained via ice-templating, and chemical vapor deposition was used to cover the filament surfaces with an aminosilane before impregnating the mats with a bio-epoxy resin. The process resulted in cellulose nanocomposites with an oriented structure and a strong fiber–matrix interface. Diffuse reflectance infrared Fourier transform and X-ray photoelectron spectroscopy studies revealed the presence of silane on the filaments. The improved interface, resulting from the surface treatment, was observable in electron microscopy images and was further confirmed by the significant increase in the tan delta peak temperature. The storage modulus of the matrix could be improved up to 2.5-fold with 18 wt% filament content and was significantly higher in the filament direction. Wide-angle X-ray scattering was used to study the orientation of cellulose nanofibers in the filament mats and the composites, and the corresponding orientation indices were 0.6 and 0.53, respectively, indicating a significant level of alignment. 

Ämnesord

Engineering and Technology  (hsv)
Materials Engineering  (hsv)
Composite Science and Engineering  (hsv)
Teknik och teknologier  (hsv)
Materialteknik  (hsv)
Kompositmaterial och -teknik  (hsv)
Engineering and Technology  (hsv)
Industrial Biotechnology  (hsv)
Bio Materials  (hsv)
Teknik och teknologier  (hsv)
Industriell bioteknik  (hsv)
Biomaterial  (hsv)
Trä och bionanokompositer  (ltu)
Wood and Bionanocomposites  (ltu)

Genre

government publication  (marcgt)

Indexterm och SAB-rubrik

cellulose nanocomposite
ice-templating
interface
orientation
mechanical properties
Inställningar Hjälp

Ingår i annan publikation. Gå till titeln Nanomaterials

Om LIBRIS
Sekretess
Blogg
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Sondera
Uppsök

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy