Hydrogen in ultrathin vanadium layers [Elektronisk resurs]
-
Andersson, Gabriella (författare)
-
Uppsala universitet Teknisk-naturvetenskapliga vetenskapsområdet (utgivare)
- Publicerad: Uppsala : Acta Universitatis Upsaliensis, 1999
- Engelska 49
-
Serie: Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1104-232X 1104-232X ; 442
-
Läs hela texten
-
Läs hela texten
Sammanfattning
Ämnesord
Stäng
- The influence of elastic boundary conditions on the thermodynamics of hydrogen in vanadium were investigated using resistometry, x-ray diffraction and nuclear reaction analysis. To provide varying lattice strain states Mo/V (110) and Fe/V (001) superlattices with thickness L of individual layers in the range 3-16 monolayers (ML) were used. In addition the thickness ratio L Fe /L V in the latter samples was varied. The results were compared with earlier work on Mo/V (001) superlattices. In the Mo/V (110) superlattices the H-H interaction was found to be repulsive in contrast to the (001) oriented samples and bulk V. This was also the case for Fe/V (001). For the thickness ratios L Fe /L V = 3/10 and 3/16 it was found that the hydrogen-depleted interface region in V was populated at lower average concentration than in the symmetric samples (L Fe L V = 1). This was related to the decreased Fe thickness. For Fe(3ML)/V(12-15 ML) samples the effects of hydrogenation on the magnetic exchange coupling between the Fe layers were investigated using neutron reflectometry. For 12 and 14 ML of V the coupling was switched continuously from antiferromagnetic (AFM) to ferromagnetic (FM) upon introduction of small amounts of hydrogen, whereas the initially FM-coupled 15-ML sampleexhibited an antiferromagnetic "resonance" at H/V ≈ 0.02. This was found to be due to changes in the vanadium Fermi surface. An intermediate state of noncollinear coupling was also observed in the 14-ML sample.
Ämnesord
- Natural Sciences (hsv)
- Physical Sciences (hsv)
- Naturvetenskap (hsv)
- Fysik (hsv)
- NATURAL SCIENCES (svep)
- Physics (svep)
- NATURVETENSKAP (svep)
- Fysik (svep)
- Fysik (uu)
- Physics (uu)
Genre
- government publication (marcgt)
Indexterm och SAB-rubrik
- Physics
- Fysik
Inställningar
Hjälp
Uppgift om bibliotek saknas i LIBRIS
Kontakta ditt bibliotek, eller sök utanför LIBRIS. Se högermenyn.